High Efficiency Medical Scintillator Lu2SiO5:Ce Studied by VUV Spectra

Get Citation
QI Ze-Ming, ZHANG Guo-Bin, SHI Chao-Shu, LIU Bo, REN Guo-Hao, TAO Ye and XU Jian-Hua. High Efficiency Medical Scintillator Lu2SiO5:Ce Studied by VUV Spectra[J]. Chinese Physics C, 2003, 27(S1): 32-34.
QI Ze-Ming, ZHANG Guo-Bin, SHI Chao-Shu, LIU Bo, REN Guo-Hao, TAO Ye and XU Jian-Hua. High Efficiency Medical Scintillator Lu2SiO5:Ce Studied by VUV Spectra[J]. Chinese Physics C, 2003, 27(S1): 32-34. shu
Milestone
Received: 2003-11-21
Revised: 1900-01-01
Article Metric

Article Views(2922)
PDF Downloads(604)
Cited by(0)
Policy on re-use
To reuse of subscription content published by CPC, the users need to request permission from CPC, unless the content was published under an Open Access license which automatically permits that type of reuse.
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Email This Article

Title:
Email:

High Efficiency Medical Scintillator Lu2SiO5:Ce Studied by VUV Spectra

    Corresponding author: QI Ze-Ming,
  • National Synchrotron Radiation Laboratory,University of Science and Technology of China,Hefei 230026,China2 Shanghai Institute of Ceramics,CAS,Shanghai 200050,China3 Institute of High Energy Physics,CAS,Beijing 100039,China

Abstract: High efficiency medical scintillator Lu2SiO5:Ce was studied by Synchrotron Radiation VUV spetra.The results show that two excitation bands in the range 250—320nm of powder sample become very weak in comparison with those of single crystal sample.The difference of the excitation band assigned to band to band transition between the two samples indicates that there are different defects in these two samples.Under VUV excitation (185nm),the emission spectrum of the two samples are similar.The emission band in the rage of 350—500nm corresponding to 5d→4f transitions of Ce3+.It can be decomposed to three sub-band which come from two types of Ce3+ luminescence centers.A new weak emission band was observed under VUV excitation.It possibly originates from the second type of Ce3+ luminescence centers of defect.