Characterization of the nanopore structures of PAN-based carbon fiber precursors by small angle X-ray scattering

Get Citation
WANG De-Hong, HAO Jun-Jie, XING Xue-Qing, MO Guang, GONG Yu, WU Zhong-Hua and Characterization of the nanopore structures of PAN-based carbon fiber precursors by small angle X-ray scattering[J]. Chinese Physics C, 2011, 35(9): 870-874. doi: 10.1088/1674-1137/35/9/016
WANG De-Hong, HAO Jun-Jie, XING Xue-Qing, MO Guang, GONG Yu, WU Zhong-Hua and Characterization of the nanopore structures of PAN-based carbon fiber precursors by small angle X-ray scattering[J]. Chinese Physics C, 2011, 35(9): 870-874.  doi: 10.1088/1674-1137/35/9/016 shu
Milestone
Received: 2010-12-04
Revised: 2011-02-13
Article Metric

Article Views(2302)
PDF Downloads(459)
Cited by(0)
Policy on re-use
To reuse of subscription content published by CPC, the users need to request permission from CPC, unless the content was published under an Open Access license which automatically permits that type of reuse.
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Email This Article

Title:
Email:

Characterization of the nanopore structures of PAN-based carbon fiber precursors by small angle X-ray scattering

    Corresponding author: ,

Abstract: The nanopore structures in precursors are crucial to the performance of PAN-based carbon fibers. Four carbon-fiber precursors are prepared. They are bath-fed filaments (A), water-washing filaments (B), hot-stretching filaments (C) and drying-densification filaments (D). Synchrotron radiation small angle X-ray scattering is used to probe and compare the nanopore structures of the four fibers. The nanopore size, discrete volume distribution, nanopore orientation degree along the fiber axis and the porosity are obtained. The results demonstrate that the nanopores are mainly formed in the water-washing stage. During the processes of the subsequent production technologies, the slenderness ratio of nanopores and their orientation degree along the fiber axis increase further and simultaneously, the porosity decreases. These results are helpful for improving the performance of the final carbon fibers.