Microstructural stability of NiO-containing spin valves annealed at room temperature

ZHANG Ai-Mei; CAI Hong-Ling; ZHAI Zhang-Yin; DU Jun; WU Xiao-Shan; JIA Quan-Jie

doi:10.1088/1674-1137/33/11/003

Chinese Physics C> 2009, Vol. 33> Issue(11) : 944-948 DOI: 10.1088/1674-1137/33/11/003

Microstructural stability of NiO-containing spin valves annealed at room temperature

Abstract
HTML
Reference
Related

PDF

Abstract：
Microstructure of NiO-containing Co/Cu/Co spin valves (CCC-SV) annealed at room temperature for nearly four years has been studied by synchrotron radiation X-ray diffraction. With the annealing time expanding, the thickness of each sub-layer remains nearly unchanged while the interface roughness varies obviously compared with that of samples without annealing. The roughness at the interface of NiO/Co decreases with the annealing time increasing for both of the samples with NiO layer on the top (TSV) and under the bottom (BSV) of CCC-SV. On the other hand, the roughness at Co/Cu interface increases with the annealing time expanding for BSV while it decreases for TSV. These results indicate that the structure of TSV is more stable than that of BSV.

References

[1]

. Berger L. Phys. Rev. B, 1996, 54: 9353-93582. Parkin S S P. Phys. Rev. Lett., 1993, 71: 1641-16443. Parkin S S P, JIANG X, Kaiser C et al. Proc. IEEE , 2003,91: 661-6804. Chopra H D, YANG D X, CHEN P J et al. Phys. Rev. B,2000, 61: 9642-96525. Chopra H D, Hockey B J, CHEN P J et al. J. Appl. Phys.,1997, 81: 4017-40196. Kim J K, HUANG D G, Lee S S et al. J. Appl. Phys., 2001,89: 6946-69487. Fujikata J, Hayashi K, Nakada M. J. Appl. Phys., 1999,85: 5021-50238. Lubitz P, Krebs J J, Miller M M et al. J. Appl. Phys., 1998,83: 6819-68219. Anthony T C, Brug J A, ZHANG S. IEEE Trans. Magn.,1994, 30: 3819-382110. ZHANG A M, WU X S, SUN L et al. J. Appl. Phys., 2004,95: 7294-729611. ZHANG A M, WU X S, SUN L et al. Applied PhysicsA-Materials Science and Processing, 2005, 81: 501-50512. ZHANG A M, WU X S, SUN L et al. International Journalof Modern Physics B, 2005, 19: 2574-257913. ZHANG A M, WU X S, SUN L et al. Nuclear Techniques,2004, 27: 485-488

[1]	Wen-Li Yuan , Zhen-Ni Xu , Jin-Li Zhang , Hong-Shi Zong . Skyrmion stability at finite isospin chemical potential and temperature. Chinese Physics C, 2020, 44(1): 014103. doi: 10.1088/1674-1137/44/1/014103
[2]	Peng-Cheng Li , Hong-Fei Zhang , Yong-Jia Wang . Stability of super heavy nuclei associated with the updated nuclear data. Chinese Physics C, 2017, 41(11): 114103. doi: 10.1088/1674-1137/41/11/114103
[3]	Shuang Ma , Ming-Wu Wen , Zhan-Shan Wang . Thermal stability and separation characteristics of anti-sticking layers of Pt/Cr films for the hot slumping technique. Chinese Physics C, 2016, 40(7): 079001. doi: 10.1088/1674-1137/40/7/079001
[4]	M. Ismail , A. Y. Ellithi , A. Adel , Hisham Anwer . Islands of stability and quasi-magic numbers for super-and ultra-heavy nuclei. Chinese Physics C, 2016, 40(12): 124102. doi: 10.1088/1674-1137/40/12/124102
[5]	Jue Zhang , Shun Zhou . Electroweak vacuum stability and diphoton excess at 750 GeV. Chinese Physics C, 2016, 40(8): 081001. doi: 10.1088/1674-1137/40/8/081001
[6]	LIU Jia , SHENG Xiang-Dong , HE Hui-Hai , ZHAO Jing , CHANG Jin-Fan , GU Min-Hao , HOU Chao , LÜ Hong-Kui . Performances and long-term stability of the LHAASO-KM2A prototype array. Chinese Physics C, 2014, 38(2): 026001. doi: 10.1088/1674-1137/38/2/026001
[7]	DENG Hai-Xiao , ZHANG Meng , GU Duan , LIU Bo , GU Qiang , WANG Dong . Simulation studies on laser pulse stability for Dalian coherent light source. Chinese Physics C, 2014, 38(2): 028101. doi: 10.1088/1674-1137/38/2/028101
[8]	CHEN Ze , HU Zheng-Guo , CHEN Jin-Da , ZHANG Xiu-Ling , GUO Zhong-Yan , XIAO Guo-Qing , SUN Zhi-Yu , HUANG Wen-Xue , WANG Jian-Song . A simulation study of a dual-plate in-room PET system for dose verification in carbon ion therapy. Chinese Physics C, 2014, 38(8): 088202. doi: 10.1088/1674-1137/38/8/088202
[9]	LIU Bo , LIU Ran , LI Quan-Jun , YAO Ming-Guang , ZOU Bo , CUI Tian , LIU Bing-Bing , LIU Jing . Study of high pressure structural stability of CeO₂ nanoparticles. Chinese Physics C, 2013, 37(9): 098003. doi: 10.1088/1674-1137/37/9/098003
[10]	XIE Wen-Qing , LI Yu-Lan , LI Yuan-Jing , YUE Qian . Performance study of the PTFE-THGEM at room and low temperature. Chinese Physics C, 2013, 37(11): 116001. doi: 10.1088/1674-1137/37/11/116001
[11]	WANG Dian-Fu , SUN Xiao-Yu , LIANG Chao . Dynamical CP violation at finite temperature. Chinese Physics C, 2012, 36(9): 805-809. doi: 10.1088/1674-1137/36/9/002
[12]	AN Zheng-Hua , SHI Feng , HU Tao , CAI Xiao , YU Bo-Xiang , FANG Jian , XIE Yu-Guang , WANG Zhi-Gang , XUE Zhen , SUN Xi-Lei , ZHANG Ai-Wu , NING Fei-Peng , ZHOU Li , SUN Li-Jun , GE Yong-Shuai , LIU Ying-Biao , WU Chong , , . Performance of MPPC at low temperature. Chinese Physics C, 2012, 36(7): 633-638. doi: 10.1088/1674-1137/36/7/012
[13]	TANG Liang , LI Xue-Qian . Discussions on the stability of diquarks. Chinese Physics C, 2012, 36(7): 578-584. doi: 10.1088/1674-1137/36/7/002
[14]	WANG Fang , LIN Lin , ZHANG He , HAO Jian-Kui , ZHANG Bao-Cheng , LIU Ke-Xin . Amplitude and phase stability studies in a DC superconducting injector. Chinese Physics C, 2011, 35(9): 855-858. doi: 10.1088/1674-1137/35/9/013
[15]	A. Maas . Describing gluons at zero and finite temperature. Chinese Physics C, 2010, 34(9): 1328-1330.
[16]	ZHANG Li-Hua , ZHAO Yu-Min . Number of spin I states for bosons. Chinese Physics C, 2009, 33(S1): 137-139. doi: 10.1088/1674-1137/33/S1/043
[17]	WANG Tie-Shan , PENG Hai-Bo , Ovsyannikov V , Kentsch U , Ullmann F , CHENG Rui , Zschornack G . Production of highly charged argon ions from a room temperature electron beam ion trap. Chinese Physics C, 2008, 32(5): 389-392. doi: 10.1088/1674-1137/32/5/013
[18]	Zheng Chunkai , Hu Jimin , Xu Furong . Studies of Nuclei Far from the Stability Line with Macro-Microscopic Model. Chinese Physics C, 1996, 20(S2): 171-177.
[19]	Chen Baoqiu , Ma Zhongyu . Description of the Properties of Nuclei Far From the β Stability Line in the Relativistic Mean Field Theory. Chinese Physics C, 1994, 18(Z1): 87-94.
[20]	Bi Pinzhen . Kaon Condensation at Finite Temperature. Chinese Physics C, 1989, 13(S1): 49-52.

Access

Get Citation

ZHANG Ai-Mei, CAI Hong-Ling, ZHAI Zhang-Yin, DU Jun, WU Xiao-Shan and JIA Quan-Jie. Microstructural stability of NiO-containing spin valves annealed at room temperature[J]. Chinese Physics C, 2009, 33(11): 944-948. doi: 10.1088/1674-1137/33/11/003

RIS(for EndNote,Reference Manager,ProCite)

BibTex

Txt

Milestone

Received: 2008-12-17
Revised: 2009-04-02

Article Metric

Article Views(2841)
PDF Downloads(663)
Cited by(0)

Policy on re-use

To reuse of subscription content published by CPC, the users need to request permission from CPC, unless the content was published under an Open Access license which automatically permits that type of reuse.

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Microstructural stability of NiO-containing spin valves annealed at room temperature

Corresponding author: WU Xiao-Shan,

Received Date: 2008-12-17

Accepted Date: 2009-04-02

Available Online: 2009-11-05

Abstract:

Microstructure of NiO-containing Co/Cu/Co spin valves (CCC-SV) annealed at room temperature for nearly four years has been studied by synchrotron radiation X-ray diffraction. With the annealing time expanding, the thickness of each sub-layer remains nearly unchanged while the interface roughness varies obviously compared with that of samples without annealing. The roughness at the interface of NiO/Co decreases with the annealing time increasing for both of the samples with NiO layer on the top (TSV) and under the bottom (BSV) of CCC-SV. On the other hand, the roughness at Co/Cu interface increases with the annealing time expanding for BSV while it decreases for TSV. These results indicate that the structure of TSV is more stable than that of BSV.

HTML

Reference (1)

Microstructural stability of NiO-containing spin valves annealed at room temperature

Abstract：

References

Access

Article Metrics

Metrics

通讯作者: 陈斌, bchen63@163.com

Email This Article